Fused Cast 33 ＃ AZS Block (RTK-AZS33)

Fused Cast 33 ＃ AZS Block (RTK-AZS33)
Fused Cast α-β-Alumina Block(RTK-M)

Fused Cast α-β-Alumina Block(RTK-M)
Fused Cast Zirconia Block (RTK-Z910)

Fused Cast Zirconia Block (RTK-Z910)
RTK-High Quality Monolithic Refractory

RTK-High Quality Monolithic Refractory
Fused Cast Mullite Block (RTK-FM/ZM)

Fused Cast Mullite Block (RTK-FM/ZM)
Fused Cast Zirconia Block (RTK-Z9540)

Fused Cast Zirconia Block (RTK-Z9540)
Fused Cast 41＃AZS Block ( RTK-AZS41)

Fused Cast 41＃AZS Block ( RTK-AZS41)
Fused Cast 36 ＃ AZS Block(RTK-AZS36)

Fused Cast 36 ＃ AZS Block(RTK-AZS36)
Fused Cast β-Alumina Block (RTK-H)

Fused Cast β-Alumina Block (RTK-H)
Fused Cast α- Alumina Block (RTK-A)

Fused Cast α- Alumina Block (RTK-A)
01
Monolithic-Refractory1.jpg
Monolithic-Refractory4.png
Monolithic-Refractory2.jpg
Monolithic-Refractory3.jpg

RTK-High Quality Monolithic Refractory

Monolithic refractories adopt self-produced high-quality raw materials, scientifically proportioned production, and provides products with different particle sizes according to the use. 
Monolithic refractories can be poured, sprayed or coated according to the needs of the site, suitable for a variety of complex shape structures, with high flexibility, a wide range of applications, and can be adjusted to meet specific needs, such as wear resistance, corrosion resistance. It also can maintain good thermal shock stability at high temperature, and is not easy to crack or flake, extending the service life.

    Contact us
    product details

    Berif Introduction

    These monolithic refractories adopt self-produced high-quality raw materials, scientifically proportioned production, and provides products with different particle sizes according to the use.
    Zircon Ramming Mix: It is used for cold repair and hot repair of tank bottom, tank side wall insulation layer and superstructure
    Zircon Castable: It is used for cold repair and hot repair of tank bottom, tank side wall insulation layer and superstructure
    Zircon Patch: It is used for cold repair and hot repair of furnace bottom safety layer and superstructure
    Zircon Ramming Mix: It is used to tamp the safety layer at the bottom of the furnace and heat repair the secondary parts of the furnace
    AZS Ramming Mix: It is used to tamp the safety layer at the bottom of the furnace and heat repair the secondary parts of the furnace
    AZS Castable: It used for cold repair and hot repair of furnace bottom, wall insulation layer and external structure.
    α-β Alumina Mortar: It is used for cold repair and hot repair of tank bottom, tank side wall insulation layer and superstructure
    α-β Alumina Ramming Mix: It is used for cold repair and hot repair of tank bottom, 
    tank side wall insulation layer and superstructure

    Performance Indexes

    PRODUCT
    CASTING
    PROCESS

    Zircon Ramming Mix

    Zircon Castable

    Zircon Patch

    Zircon Ramming

    Max
    ZrO2 % 64±2 （≥1560°C×2h） 64±2 （≥1560°C×2h） 64±2   64±2 （≥1560°C×2h）
    AI2O3 % /     /
    Fe2O3 0.5 0.5 0.5 0.5
    DENSITY (g/cm3) 1200°C×3h 3.45 3.5 3.45 3.40
    MAXIMUM GRAIN SIZE (mm)   4 4 4
    MOISTURE COTENT 3-5 5-7 3-5 3-5
    COLD PRESSING STRENGTH 45 50 45 45
    FIRING SHRINKAGE 0.3 0.3 0.3 0.3
    OPERAING TEMPERATURE 400-1600 100-1600 400-1600 400-1600
    APPLICATION It is used for cold repair and hot repair of tank bottom, tank side  wall insulation layer and superstructure It is used for cold repair and hot repair of tank bottom, tank side  wall insulation layer and superstructure For cold repair and hot repair of furnace bottom safety layer and superstructure It is used to tamp the safety layer at the bottom of the furnace and heat repair the secondary parts of the furnace
    PRODUCT
    CASTING
    PROCESS

    AZS Ramming Mix

    AZS Castable

    α-βAlumina Mortar

    α-βAlumina Ramming Mix
    ZrO2 % 28±1 29±1 - -
    AI2O3 % /      
    Fe2O3 0.5 0.5 0.5 0.5
    DENSITY (g/cm3) 1200°C×3h 2.9 3.0 2.9 3.0
    MAXIMUM PARTICLE SIZE (mm) 5 10.5 4 5
    MOISTURE COTENT 3-5 6-8 3-5 6-8
    COLD PRESSING STRENGTH 50 75 50 70
    FIRING SHRINKAGE 0.2 0.2 1500°C×3h0.1 1500°C×3h0.1
    OPERAING TEMPERATURE 100-1500 100-1500 100-1500 100-1500
    APPLICATION It is used to tamp the safety layer at the bottom of the furnace and heat repair the secondary parts of the furnace It used for cold repair and hot repair of furnace bottom, wall insulation layer and external structure. It is used for cold repair and hot repair of tank bottom, tank side  wall insulation layer and superstructure It is used for cold repair and hot repair of tank bottom, tank side  wall insulation layer and superstructure